Complementary manufacturing operations

Applications of complementary operations on a sintered component allow to improve one or more characteristics not directly achievable from the basic process.


It consists of compacting again the part inside a rigid mould which has the symmetrical opposite shape of the part.
Sizing can have several purposes:
– Increasing the dimensional precision in diameter, reaching up to IT 5. The densification degree is lower than 4%.
– Creating relief geometrical details not feasible in the compacted part, or improving roughness.
– Densification. The applied densification degree is 7-10%, and it is also known as Coining. Densities up to 7.6 g/cm3 are possible.


Impregnation consists in filling pores with a chemical product:
 Oil impregnation. Oil contained in the pores can act as lubricant of a bearing-shaft interface, hence self-lubrication is provided.
 Plastic or resin impregnation provides sealing. This operation is quite common as preparation of the part before coating/plating.
 Copper impregnation, called Infiltration. It consists of sintering the part together with a pressed copper plate on it. Copper is molten during sintering, and becomes infiltrated inside the pores by means of capillarity. Infiltration is used to increase the mechanical strength and toughness of low alloyed sintered steels.


Sintered components can be sometimes machined when a shape or tolerance not achievable by compacting is required. Sintered parts support all conventional machining operations, ie., turning, milling, drilling, threading, grinding, lapping, reaming, polishing, and so forth.


Deburring is applied to remove burrs inherent to compacting process. Burrs are removed either in bulk (tumbling, shot blasting, …), or on a unit basis (brushing, polishing, electrolytic deburring, …). Bulk deburring is sometimes used to provide an homogeneous surface aspect, or a very low roughness.


Cleaning operations are used to reduce or eliminate the amount of pollutants, solid or liquid, that a part may contain. There are many techniques, depending on material, type of pollutant, and required specifications.


This is a thermal cycle of controlled oxidation of a steel, carried out in continuous furnaces with water steam. A magnetite layer coat is formed on the part surface and porosity. Its application on a component increases its compression strengthseals its porosity, and improves its environmental corrosion resistance.


A heat treatment is a thermal cycle that modifies the material properties. They are typically applied to increase hardness and strength of the component. The main surface or core heat treatments are: quenching, case hardening, and carbonitridingInduction hardening is used to increase hardness in a local area of the part. Other possible treatments are ion nitridingoxynitrocarburizing, or annealing.
A particular case are the sinter-hardened components, which are made of a special type of steel that becomes hardened in the sintering furnace during the cooling.


It is a material deposition on the component surface, which modifies the surface properties without changing the base metal chemical composition. Coatings are applied to fulfil functions under fatigue, wear, friction, or corrosion protection.
Sintered parts accept almost all conventional coatings, like zinc plating, chromium plating, nickel plating, phosphating, metallisation, PTFE, and other special coatings.


Sintered parts are susceptible to be joined to other sintered parts or to components made from other technologies. Typical joining techniques are welding, brazing, sinter-bonding, fitting, sticking, riveting, over-moulding, etc.

AMES may recommend the most appropiate material and design to meet your needs

powder metal manufacturing process
Basic manufacturing process
Sintered components should be designed based on several shape recommendations, aimed at making compacting feasible, as well as to minimize manufacturing costs
Recommended shapes
Advantages of sinterng
Advantages of sintering
typical dimensional tolerances achievable in a sintered part
Dimensional accuracy